Sign In | Join Free | My xpshou.com
China Shenzhen Dallast Technology Co., Ltd. logo
Shenzhen Dallast Technology Co., Ltd.
China's most high-quality hydraulic cylinder supplier
Site Member

7 Years

Home > Chrome Plated Rod >

Hydraulic Cylinder Piston Hollow Chrome Plated Rod Bar NSS 500 Hours 42CrMo

Shenzhen Dallast Technology Co., Ltd.

Hydraulic Cylinder Piston Hollow Chrome Plated Rod Bar NSS 500 Hours 42CrMo

  • 1
  • 2
  • 3

Brand Name : DALLAST

Model Number : Model

Certification : SGS TUV

Place of Origin : CHINA

MOQ : 1

Payment Terms : T/T

Supply Ability : 100000PCS/YEAR

Delivery Time : 15-25DAYS

Packaging Details : Wooden box

Material : 45# 42CrMo

Color : Black

NSS : Endure 300;500;800hours

Type : Hollow/Solid Rod

Application Environment : At sea or in harsh environments

Surface hardness : >HV850

Contact Now

42CrMo Hydraulic Cylinder Piston Hollow Rods Hard Chrome Plated Steel Bar NSS 500 Hours


Material :42CrMo

Color :Black

NSS:Endure 300;500;800hours

Type:Hollow/Solid Rod


Application Environment:At sea or in harsh environments

Surface hardness:>HV860

SURFACE ROUGHNESS:Ra≤0.2 micron and Rt≤2 micro

TOLERANCES ON DIA:ISO f10 on the diameter

Testing Standing une-en iso9227:2017

· Sal solution: 50 (+/- 5) g/l of NaCl. Water is demineralized and salt purity is 99.5%.

· Environmental temperature: 35 °C.

· pH of salt solution is 6.8.

· Volumen of salt solution is 38.4 ml/day.

· Density of salt solution is 1,030 g/cm3.

· Spraying is 1.5 (+/- 0.5) ml/h.

Test Result :NSS can endure 300 hours ;500 hours; 800 hours

SGS NSS Testing Report TUV NSSTesting Repopt

Heat treatment

1.Quenching with fire about 860 °C, placed in furnace box

2. After quenching, put into the oil tank to cool from the box furnace

3. After cooling, the first time tempering: tempered at 640 °C and the hardness is controlled at about HRC28-32, the first time tempering cooling is used Water-cooled.

4. Straightening: The outer circle is controlled by 200 um(0.2mm) ;

straightening equipment:

three-roller straightening machine;

hydraulic straightening machine (multipoint straightening)

5. The second tempering removes the hard force, the temperature is about 480 °C, and Keep warm for 2 -2.5hours ; release 80% more or less

In the whole crafts process, there are 2 times remove hardening forces: the first remove hardening force in the heat treatment process, hardening force remove is about 80%; the second remove hardening force in the surface treatment process, hardening force remove is about 90%-95%. Therefore, the piston rod is not easily deformed during use or transportation.

CHEMICAL COMPOSITION

Material C% Mn% Si% S% P% V% Cr%
Ck45 0.42-0.50 0.50-0.80 0.04 0.035 0.035
ST52 0.22 1.6 0.55 0.035 0.04
20MnV6 0.16-0.22 1.30-1.70 0.10-0.50 0.035 0.035 0.10-0.20
42CrMo4 0.38-0.45 0.60-0.90 0.15-0.40 0.03 0.03 0.90-1.20
40Cr 0.37-0.45 0.50-0.80 0.17-0.37 0.80-1.10

MECHANCIAL PROPERTIES

Material T.S N/MM2 Y.S N/MM2 E%(MIN) CHARPY CONDITION
CK45 610 355 15 >41J NORMALIZE
CK45 800 630 20 >41J Q + T
ST52 500 355 22 NORMALIZE
20MnV6 750 590 12 >40J NORMALIZE
42CrMo4 980 850 14 >47J Q + T
40Cr 1000 800 10 Q + T

Hydraulic Cylinder Piston Hollow Chrome Plated Rod Bar NSS 500 Hours 42CrMo

Hydraulic Cylinder Piston Hollow Chrome Plated Rod Bar NSS 500 Hours 42CrMo

Hydraulic Cylinder Piston Hollow Chrome Plated Rod Bar NSS 500 Hours 42CrMo


Product Tags:

chrome plated steel tube

      

piston rod cylinder

      
China Hydraulic Cylinder Piston Hollow Chrome Plated Rod Bar NSS 500 Hours 42CrMo wholesale

Hydraulic Cylinder Piston Hollow Chrome Plated Rod Bar NSS 500 Hours 42CrMo Images

Inquiry Cart 0
Send your message to this supplier
 
*From:
*To: Shenzhen Dallast Technology Co., Ltd.
*Subject:
*Message:
Characters Remaining: (0/3000)
 

Friendly Links: www.everychina.com

Home| Products| Suppliers| Quality Suppliers| Site Map |About Us |Contact Us |Help |关于我们 |联系我们

Copyright © 2009 - 2024 xpshou.com. All rights reserved.